Post by 808ministroke on Mar 17, 2024 2:04:05 GMT -5
|
|
|
Post by aeroxbud on Mar 17, 2024 4:14:18 GMT -5
Is that the Piaggio lump? I have seen a few Piaggio cases break there. It could be welded, but that is a high stress area. I would personally replace that case half.
|
|
|
Post by 808ministroke on Mar 17, 2024 13:37:51 GMT -5
Is that the Piaggio lump? I have seen a few Piaggio cases break there. It could be welded, but that is a high stress area. I would personally replace that case half. dang so this is a common occurrence, I feel a torsion arm would have prevented this . I am not ready to throw in the Towel this block has been though hell with me me buddy said try alumaloy to weld it with using a map gas torch. any welders here with opinions on that? 190 mech I'm looking at you.
|
|